Why We Love Cryogenic Deflashing Machine (And You Should, Too!)

Moulding is a common method to produce rubber goods today. And if you are a rubber moulder; I bet that, like any other manufacturer, you are constantly exploring technology for gains in productivity. And one area where you quickly stand to gain is in deflashing.

Your moulded rubber parts must undergo a finishing process to remove excess rubber flash before they are cleared for final inspection and packing. And this process is termed deflashing.

Most moulded rubber goods producers are currently deflashing manually. This means dozens of workers, seated at small work stations, would take each part and trim the excess rubber off with scissors, knives or grinders.

Obviously, this hand deflashing has several drawbacks. The quality of work done by hand is often inconsistent. This apart, as labour wages rise, your hand deflashing becomes expensive and unsustainable.

This is where automation of deflashing process assumes importance and Why We Love Cryogenic Deflashing Machine.

If you are manufacturing any of these – O-rings & gaskets, catheters and other in-vitro medical items, Insulators and other electric / electronic items, Valve stems, washers and fittings, Tubes and flexible boots, or Face masks & goggles; you too should love Cryogenic Deflashing as a process to remove flash from your moulded rubber parts. Here’s why.

Cryogenic Deflashing Machine

Image from Web


Deflashing machine also known as deburring machine. Though this cryogenic deflashing technology is in existence for over 50 years, its ‘practical introduction’ happened about 20 years back. Its popularity is on the rise in last 15 years.

This process uses liquid nitrogen, high-speed rotation and media (shot blast) in varying combinations to remove the flash in a highly precise, economical and practical manner.

There are two basic styles of cryogenic deflashing machine – basket and belt. The basket style was designed to process small parts and offers 100% parts containment. The belt style was designed for larger/heavier parts which require more room to tumble and a stronger rotation system.


A typical cryogenic deflashing machine consists of a stainless steel cabinet insulated with dense polyurethane foam. Located inside the cabinet are the blast chamber, the liquid nitrogen nozzle, and the opening for the throw wheel.

Plastic shots ranging size from 0.15 to 1.4 mm are deployed. These shots do not cause rust or part contamination. All major components of the machine (motors, bearings, etc.) are located outside of the cabinet and isolated from the temperature variations and moisture.

These are maintenance-friendly design and also reduce component failure in your machine.

In your machine, there must be room within the blasting chamber for the parts to tumble because it is the tumbling action that exposes the parts to both the Nitrogen and the media stream. The actual size of the chamber should be at least twice the size of your load.

Configuration of a Deflashing Machine - Samstal

Image from Web

Manufacturers of cryogenic deflashing machines offers you options such as programmable controllers with numerous deflashing “recipes” for automatic operation, networking capabilities, bar coding abilities, message centers, reporting, historical data etc.


Your moulded parts are placed in a perforated stainless steel basket and inserted into a highly insulated blast chamber. Liquid nitrogen is injected into this chamber in which the basket with your moulded rubber parts is mechanically rotated to expose all parts to the blast media.

Liquid nitrogen lowers the temperature (some cases up to -140°C) while freezing the rubber to make it brittle. The physical properties of your moulded rubber parts are not affected during the deflashing process.

A unique high-speed (up to 8,000 rpm) impeller directs and throws plastic shots at the tumbling parts into the rotating basket. Travelling at high-speed, these small pellets cleanly trim off the brittle flash leaving a high quality, flash less molding. The machine separates reusable media from debris (flash and dust).

In some instances, cryogenic deflashing does not utilize a blasting action, relying instead only on the tumbling of the parts to remove flash on the outer edges.

Parts that have thin flash can be quickly and thoroughly cryogenic deflashed. Cryogenic Deflashing process is exceptionally good at removing the inner dimensional and complex flash in your products that cannot be removed by any other method.

The average cycle time can range from 1.5 – 10 minutes depending on the number of parts per batch (which is, dependent on the size of your moulded parts); flash thickness; wheel speed; and size of media used.

Cryogenic Deflashing Machine - Barwell

Click on the Image to Watch Video (11:29 Mins Long)

To consistently get a quality-finished-part, you have to consistently put in a quality unfinished-part. This means,

  • Flash: Make the flash of your moulded product as thin as possible (<0.3mm), with as good a flash base as possible, or, in the case where sealing surfaces are involved, try to move the flash away from the critical areas.
  • Overflows should, if they are necessary for your molding process, be moved as far away from the part as possible.
  • Tear trim design was developed to eliminate the cryogenic deflashing operation. The overflow is placed extremely close to the part so that, when this overflow is removed by hand, no flash remains. (If there’s tear trim…Keep atleast 0.5mm from parts)
  • Parting Lines: Your moulded parts need a clear, consistent demarcation of flash. For best results, the parting line should not exceed 0.127 mm thickness.

It is important you understand that no cryogenic deflashing unit will eliminate your molding problems.


While liquid nitrogen consumption could be a concern for some manufacturers, Cryogenic deflashing provides you various advantages over manual deflashing and other traditional deflashing methods.

  • Greater Productivity. Cryogenic deflashing trims parts in seconds.
  • Better Product Quality. The process maintains part integrity and critical tolerances.
  • Since it is a batch process, the price per piece is far less as many more parts can be processed in a given amount of time.
  • The process offers consistent results from part to part.
  • Cryogenic deflashing extends mold life. Rather than replace or repair a mold (which typically involves downtime and high cost), the parts can be deflashed. This is typical of parts molded at the end of their product lifetime.
  • Simple Operation. Highly automated, today’s cryogenic deflashing equipment is easy to use.
  • The process is computer controlled, therefore removing the human operator variable from the process.
  • Cryogenic deflashing is non-abrasive.
  • The cost per part is generally well below any alternative technique.
  • Environmentally Sound. The nitrogen cryogen can be recycled or vented safely to the atmosphere. In addition, cryogenic deflashing systems are typically enclosed to minimize noise.

Lastly, at a price ranging from US $45,000 to $130,000 (depending on your country of procurement and features), the new generation cryogenic deflashing units has a wide appeal to moulders of different volume levels and product mixes.

Do you agree? 

If you liked this article, please do share with your colleagues, customers and friends. And If you would like to be informed of our articles regularly, please register with us for free updates today.


Editor’s Pick: Injection Moulding Of Rubber Product (Part 2)

Continuing with Part 1 of this article, by Dr.S.N.Chakravarty, President – Elastomer Technology Development Society and Ex-Chairman, Indian Rubber Institute (IRI).

Now, let us look  more deeply into Injection moulding process.

Types of Injection Moulding Machines

The following distinctions may be made between the machines used:

  • The toggle or hydraulic mould closing mechanism
  • The plunger or screw type plasticating and injection unit
  • The plunger screw type plastication unit may be further subdivided into those with and those without reciprocating movement.

The fully hydraulic mould clamping mechanism is preferred today.

Desma Injection Moulding Machine

Image: Desma

Operation Principles: Three types of injection moulding operations can be distinguished according to the differences in tool design and process sequence:

  • The conventional
  • The injection forming and
  • The transfer-injection moulding methods

The essential advantage of screw plasticating machines is the very short cycle time which is very important for high volume production, e.g. using rotary table mould arrangements.

One of the requirements for automated rubber injection moulding is to produce a rubber compound of the highest possible uniformity, which is still quite a difficult task even today.

Other important factors depending on controlled mixing are those of optimum and uniform reheological properties, the dispersion of the ingredients  in the compounds, and computer-aided optimization of the vulcanization process, especially for thick-walled moulding. Compounds with consistent processing properties can now be produced using automatically controlled internal mixers.

Another problem is that of automatically feeding the raw material into the injection moulding machine. The strip feeding method in its original form is too imprecise and needs constant manual attention. Recently, however, the strip feeding method has been refined by using strips of precise dimensions wound on drums, allowing limited periods of automated production. Another method used is to feed the compound into the injection moulding machine in granulated form. This may prove to be the best method for fully automated production in the future.

The manufacturer who has installed injection moulding equipment (or who is considering so doing) must consider four general questions:

  • What rubber to use ?
  • How to adjust machine controls ?
  • Which formulations ?
  • What end properties to expect ?

Injection moulding is specially suitable for the mass production of high quality precision components.

For a given barrel temperature, the higher the heat build-up the shorter the cure time. Alternatively, for a fixed injection temperature, the higher the heat build-up the lower the temperature at which the barrel of the machine may be set thus minimizing the danger of premature vulcanization (scorch) in the barrel.

Injection moulding process for elastomeric compound have certain specific advantages over the moulding process.

In Compression and Transfer moulding,  elastomer is pushed into the mould cavity gradually as the mould closes.  Therefore  in the process, though the elastomer gets in contact with the hot surface of the mould , it is not subjected to any pressure, which is  created when the mould is at closing face.  For vulcanization, both temperature & pressure are required.

In injection moulding, mould first closes fully and elastomer is pushed into the mould with high speed.  The cavity of the mould is very quickly filled and a pressure is developed within a very short time, thereby, triggering the process of vulcanization.

In compression moulding process or in transfer moulding process, the flow of material stops immediately when the mould is completely closed. Therefore, typical problems like generation of small gases and vapour, shrinkage of elastomer after vulcanization cannot really be rectified in the above process.

In injection moulding machine there is always a special feature which is known as Post Injection Pressure. Even when the cavity is completely filled and the process of vulcanization has started, the injection unit still continue to push in the elastomer compound for a reasonable length of time ensuring completely porosity free moulding.

REP Injection Moulding Machine

Video of Compact Multisation Molding Machine. Image – REP

Advantages of Injection Moulding

  • Allow automation to be introduced into the moulding operation.
  • Simplifies preparation of rubber: cutting, shaping and weighing of blanks eliminated.
  • Cure times reduced to one-tenth or less compared with compression moulding
  • Materials, trimming and inspection costs reduced.
  • Product quality improved: better dimensional control and more uniform physical properties.

Cure time is considered as a measure of productivity obtainable. This is the time elapsed between injection and opening the mould. For a given set of operating conditions, cure time depends on the thickness of the product.

Early work showed that barrel temperature was one of the most important factors affecting injection temperature.

As Screw speed increases, rubber in the barrel of the injection machine becomes hotter and it is possible to obtain higher injection temperatures and shorter cure times. Cure time, assessed by the hardness of the top, center and bottom of the moulding, closely follows the injection temperature and illustrates that under the prevailing back pressure and barrel temperature conditions there is an optimum screw speed.

Injection temperature increases with elevation of barrel temperature. When there is no screw delay in operation, temperatures above optimum level causes premature vulcanization of rubber in the barrel.

Screw-back pressure is the adjustable hydraulic pressure which acts to pressurize the plasticized rubber in the injection chamber during screw rotation. Injection temperature increases with screw-back pressure.

As the Nozzle orifice diameter is reduced, the injection temperature rises but, below a diameter of 2mm (0.075 in), it levels off .

With a relatively wide nozzle orifice (3.2mm; 0.125 in), an increase in the injection pressure gives a steady rise in injection temperature and a useful reduction in injection time.

Machine manufacturers advise use of 80-90 percent of the maximum available pressure to save wear and tear on the machine.


The principles of successful compounding for injection moulding follow the normal rules. The choice of curing system determines properties such as scorch rate, cure rate, reversion resistance, modulus, strength, resilience and ageing resistance. Control of mix viscosity can be used with caution to optimize mould filling time and hence cure time. Required stiffness, strength and cost can be obtained by selection of filler at an appropriate volume loading.

Physical properties (tensile strength, modulus, etc.) of injection moulded components can be expected to be very similar to those made by compression moulding although the modulus of injection moulded samples may be equal to  that of compression moulded samples, the tensile strength tends to be higher. There is also published evidence that injection moulded components are similar to or better than compression moulded ones in respect of elongation at break, tear strength, hardness, resilience and oven ageing resistance. There have also been claims that in some circumstances certain properties (e.g. Dynamic properties ) of injection moulded products are superior.

Particular interest attaches to the injection moulding of thick  components such as engine mounting and shock absorbers – traditional high-quality natural rubber products.  The greatest benefits of injection moulding are obtained when moulding thick sections since injection at  high temperature saves the time required to heat rubber by the relatively slow transfer of heat into a mix of poor thermal conductivity.

Compound with higher Rubber Hydrocarbon content (RHC) is preferable for injection moulding process.

Advantages and Disadvantages of Injection Moulding Process

A comparison of injection moulding with compression moulding shows the following advantages and disadvantages:

Advantages are for example:

  • Reduced preparatory labour
  • Transport and storing of the cut reforms is eliminated.
  • Considerably shorter vulcanization times because of homogeneously preheated material.
  • More homogeneous degree of vulcanisaiton of the finished part at high injection temperature.
  • No bumping.
  • Faster removal of the finished parts
  • Simplification of de-flashing
  • Lowering of the waste and scrap rate
  • Possibility of automation

These advantages are contrasted by the disadvantages of considerably higher investment costs for moulds and machinery. The injection moulding process can not also handle as high volumes as compression moulding.

Economic Efficiency

Which method is most economical for the production of moulded parts, compression moulding with low investment costs but with higher production costs or injection moulding with higher investment costs, depends to a high degree on the number of parts to be produced. Below certain limits it is advantageous to work with low investments but higher wave costs while for high volume production runs  higher investments may be preferable.

However, considering improvement in product quality leading to higher performance  and longer life made by injection moulding process, it is preferable to go for the same.

Taking into account of all factors associated with injection moulding, namely – Capital Investment, higher precision of working, higher (improved) compound cost, Qualified & experienced Technologist needed etc. would lead to a higher cost of the finished product.

Besides choice of Machine & Process one has to keep in mind that performance of a rubber product depends on many other factors which need equal attention. These are, for example, for certain metal to rubber bonded items used by Indian Railway.

  1. Application condition
  2. Environmental condition – Oxygen, Ozone, Fatigue, Displacement Amplitude etc.
  3. Compression under continuous load
  4. Geometry / design of the product – FEA Analysis results


Simultaneously to consider which aspects can improve product performance.  For example,

Compound Quality – Homogeneous Mixing / Mix quality (Kneader is not a suitable substitute of internal mixer)

Rheometer provides cure characteristics information but does not indicate mixing quality .

Homogeneity of the compound sheet

Lower Heat Built-up (Resilience /Hysteresis)

Ageing resistance over longer period

Summarizing, it is quite clear that only particular machine or process usage will not lead to improved product performance but combination of all related points development is essential to achieve the desired goal. Any specification should be drawn only after ascertaining the results of these studies.


  1. Injection moulding of natural rubber – MRPRA Booklet
  2. Rubber Technology Handbook – W. Hofmann
  3. A.I. Isayev  & M. Wan – Rubber Chemistry & Technol. 69, No. 2, p. 277, & 294, 1996
  4. K. Yakemoto, T. Shiroganeya, H. ITO & T. Sakai. International Conference on Rubber, Calcutta, Dec. 12 -14, 1997, p.73

If you liked this article, please do share with your colleagues, customers and friends. And If you would like to be informed of our articles regularly, please register with us for free updates today.


Editor’s Pick: Injection Moulding Of Rubber Product (Part 1)

Here is an informative piece on injection moulding of rubber products. This article is sent to me by Dr.S.N.Chakravarty, President – Elastomer Technology Development Society and Ex-Chairman, Indian Rubber Institute (IRI).

Moulded rubber products, including rubber to metal bonded items, are manufactured by following process world-wide. Choice of process depends on different factors like Product Geometry, Type of Polymer, Volume, Cost Vs Market Price realization, Manpower & Space etc.

  1. Compression Moulding
  2. Transfer Moulding
  3. Injection Moulding

All the process are well established and widely used. Each process has certain advantages & disadvantages. To get optimum result, you all need suitably developed compound & manpower besides right machine & process.

Compound is developed to meet requirement of laid down specification including special requirement (e.g. dynamic fatigue, heat development, tear resistance, load deflection, etc.) and retention of properties on ageing for specific period at elevated temperature. The later indicates approximate idea for product performance & life. All these obviously have bearing on cost factor.

For different moulding process three major properties or compound behavior is to be considered – Compound Flow Characteristics, Mooney Viscosity and Scorch Characteristics. Each process calls for adjustment of these parameters for suitable working.


Primary purpose of moulding is to provide shape & size of the product. Porosity & Knit in the product are to be avoided. Porosity is caused by moisture in the compound & moulding pressure and Knit by improper compound flow.

In case of Compression moulding, preparation of Blank (shape, size, weight) plays important role to control mould flow / avoid air entrapment and excess flash.

Compression Moulding Schematic -

Compression Moulding – (Left) Open mould With elastomer blank placed in the cavity; and (Right) Mould closed forming the finished product profile. Image: JW Elastomer Engg Guide

This point is not necessary for Transfer or Injection moulding where feeding system & wastage of semi-scorched compound are more important factor.

Transfer Moulding

Transfer Moulding – (Left) Open mould With elastomer blank placed in the transfer pot; and (Right) Mould shut with elastomer injected into the cavity. Image: JW Elastomer Engg Guide

Basics of Injection Moulding

Injection Moulding is an important processing technique for converting elastomeric materials into final products. The injection moulding machine automatically performs: raw material feeding, heating, polymer mix plasticization, and mould injection; all operations are performed under controllable conditions of temperature, time, speed, and pressure.

Some peculiar problems arising during injection moulding are associated with the drastic change in rubber compound rheological properties which occur upon vulcanization. In particular, during the filling stage, the rubber compound in the mould-filling process. This is a phenomenon that may lead to the loss of processability of the rubber compound and incomplete mould filling.

Rubber compound or thermosets go through an irreversible chemical change during the forming process. Thus, the critical issue in modeling the injection moulding process for such polymeric materials, is developing a viscosity model that can accurately describe the reheological and chemo-rheological behavior.

As Injection Moulding of Rubber compounds becomes an increasingly important moulding process, an understanding of the nature of coupling the rheological behavior with cure kinetics of rubber compounds and the process itself becomes paramount. Effective control of product quality, as well as the ability to optimize moulding conditions, will depend on a further development of such an understanding.

During Injection Moulding, the Rubber compounds are subjected to high shear rates and as a result experience a thermal history leading to chemical reaction (cross linking). It is recognized that the processibility of a rubber compound is predominantly determined by its viscosity which is balanced by tow effects: the drastic decrease in viscosity with increasing shear rate: and a significant increase in viscosity following the onset of vulcanization. Thus, different rubber compounds not only display different rheological properties, by also possess different chemo-rheological behavior.

Injection Moulding

Injection Moulding. Image: JW Elastomer Engg Guide

It is seen that an increase in the inlet temperature does not significantly reduce the cycle time needed to reach a specified cure level. One cannot further raise the inlet temperature to achieve a shorter cycle time due to the possibility of curing in the barrel. Therefore, the distribution of state-of cure in the moulded rubber articles is strongly dependent upon the mould temperature and less dependent upon the inlet temperature.

It is interesting to know how the injection speeds affects the state-of-cure achieved during the same mould cycle duration. For this purpose experiments were conducted in which the injection speed was set  at a definite speed. At this injection speed the calculation shows that there is no cure during the filling stage.

A comparison is made between the predicted and measured gap-wise distribution of state-of-cure in mouldings obtained where cure occurs during filling by  lower injection speed, and where it does not occur during filling at higher injection speed. In the later case, the ultimate state-of-cure achieved in the cure stage is the overall state-of-cure achieved during entire moulding cycle.

In the case when cure occurs during filling, the overall state –of-cure for the entire moulding cycle is the state-of-cure at the end of filling plus the state-of-cure further developed during the cure. Surprisingly, both experimental and predicted gap-wise results show that a higher stat-of-cure is obtained at higher injection speed for the same moulding cycle.

This can be explained by the fact that the rubber material gets into the cavity much faster and therefore has a much longer time to cure in the cavity.

The development of the state-of-cure in the post-filling stage indicated that the mould temperature and injection speed strongly affected the evaluation of state-of-cure within the moulded parts. The effects of the inlet temperature on the state-of-cure was found to be insignificant.

With the increasing demands for high quality and productivity in injection moulding, it has become more important to keep consistently constant dimensional precision. Various properties of polymer such as melt fluidity and density are dependent highly upon temperature. Therefore the consistency in quality is primarily dominated by the temperature variations of mould wall and / or polymer in the barrel.

Fluctuations of these temperatures, however, are indispensable to some extent, due to the heat exchange among polymer, mould, machine and environment, and transient temperature change at the start-up, etc. An adaptive holding pressure control system was developed to get constants product weight by changing holding pressure adapted to the temperature variations.

In Part 2, you will look more deeply into Injection moulding process.

If you liked this article, please do share with your colleagues, customers and friends. And If you would like to be informed of our articles regularly, please register with us for free updates today.